- CLASSIFICATIONSuspension PVDF Powder FL-2000
Categories PVDF Album View larger image Brand FOTECH CAS No. 24937-79-9 Type Synthetic Resin and Plastics Purity 99% Terms of Payment L/C, D/A, D/P, T/T Download DOC 
Update Time 2020-02-29 Detail InformationSuspension PVDF Powder FL-2000
(Li-battery adhesive)
PVDF FL-2000 homopolymeris an ultra high viscosity grade that gives the best adhesion ideal for itsusage in lithium batteries.
General
Features
Homopolymer; ultra high viscosity
Uses
Batteries; Binder
Forms
White powder
Physical Properties
Typical Value
Test Method
Density（g/cc）
1.77~1.79
ASTM D792
Particle size（μm）（D50）
≤50
ISO 22412
Water Absorption（%）(Time 24 hr)
≤0.040
ISO 62
Molecular properties
Molecular weight（Da）
750,000~1,200,000
GPC,DMAC,ISO 16014
Intrinsic viscosity（dl/g）
2.5~4.5
30℃,DMAC
molecular weight distribution
1.8-2.3
GPC,DMAC,ISO 16014
Thermal Properties
Melting Point（℃）
169~173
ASTM D3418
Crystallization Temperature(DSC peak)（℃）
137~144
ASTM D3418
Glass Transition Temp, Tg（℃）
-40
ASTM E1356
Decomposition Temperature（℃）
375
1% wt. loss / in air
Crystallization Heat（J/g）
50.0~56.0
ASTM D3417
Heat of Fusion（J/g）
55.0~66.0
ASTM D3417
Electrical Properties
Surface Resistance（ohm）
≥1.00E+14
Voltage<1V
After 2 min—500V
ASTM D257
Electrical Resistivity（ohm·cm）
≥1.00E+14
Intensity=10mA
After 2 min@23℃
ASTM D257
Process safety instructions
(1). This product should be processed under 260℃, to avoid producing toxic gases.
(2). PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds.
(3). Operators should take good care of personal protection during the use procedure and processing.
Packaging andstorage
PVDF is packed in PE plasticbag contained in a 25Kg or 50Kg drum. It must be stored in clean, cool, dry place.
Please send your message to us
Zhejiang Fotech International Co.,Ltd.
The mission of Fotech is to provide a customer driven approach in delivering highest quality products...